Scope

EN 10269 X15CrMo5-1 Specification is a European Standard that specifies requirements for semi-finished products, bars and rods for fasteners with properties specified at elevated and/or low temperatures made of non-alloy and alloy (including stainless) steels and nickel alloys.
The requirements of this standard may be applied also to the finished fasteners.
The general technical delivery conditions in EN 10021 also apply to products supplied in accordance with this European Standard.
NOTE : Once this European Standard is published in the EU Official Journal (OJEU) under Directive 97/23/EC, presumption of conformity to the Essential Safety Requirements (ESRs) of Directive 97/23/EC is limited to technical data of materials in this European Standard and does not presume adequacy of the material to a specific item of equipment. Consequently, the assessment of the technical data stated in this material standard against the design requirements of this specific item of equipment to verify that the ESRs of Directive 97/23/EC are satisfied, needs to be done.

Related Specifications of X15CrMo5-1 Bolting

DIN 267 ISO 3506-5 BS EN 10088-3

X15CrMo5-1 Chemical composition

Cast Analysis A

Material designation Chemical composition, % by mass
Name Number C Si Mn P
max.		 S
max.		 Al tot B Cr Mo Ni V Others
X15CrMo5-1 1.7390 ≤ 0,18 ≤ 0,40 0,30 to 0,80 0.025 0.015 - - 4,0 to 6,0 0,45 to 0,65 - - -
  • a Elements not listed in this table may not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All appropriate precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the usefulness of the steel.
  • b A controlled sulphur content of 0,015 % to 0,030 % improves the machinability and is therefore recommended and may be agreed at time of enquiry and order. For weldability, a controlled sulphur content of 0,008 % to 0,030 % is recommended and may be agreed at time of enquiry and order.
  • c For requirements regarding magnetic properties up to a maximum of 0,28 % C.

Permissible product analysis tolerances on the limiting values given in for the cast analysis

Element(s) Specified limits, cast analysis
% by mass		 Permissible tolerance a
% by mass
C < 0,03 ± 0,005
≥ 0,03 ≤ 0,20 ± 0,01
> 0,20 ≤ 0,50 ± 0,02
Si ≤ 0,40 ± 0,03
> 0,40 ≤ 1,00 ± 0,05
Mn ≤ 2,00 ± 0,04
> 2,00 ≤ 7,0 ± 0,10
P ≤ 0,045 +0.005
S ≤ 0,015 +0.003
> 0,015 ≤ 0,035 +0.005
N ≤ 0,040 ± 0,005
> 0,040 ≤ 0,18 ± 0,01
Al ≥ 0,015 ≤ 0,08 +0,01
-0,005
> 0,08 ≤ 0,35 ± 0,05
> 0,35 ≤ 1,80 ± 0,10
B ≤ 0,010 ± 0,000 5
> 0,010 ≤ 0,10 ± 0,005
Cr ≤ 2,00 ± 0,05
> 2,00 < 10,0 ± 0,10
≥ 10,0 < 15,0 ± 0,15
≥ 15,0 ≤ 21,0 ± 0,20
Cu ≤ 0,50 +0.05
> 0,50 ≤ 4,0 ± 0,10
Mo ≤ 0,60 ± 0,03
> 0,60 < 1,75 ± 0,05
≥ 1,75 ≤ 3,00 ± 0,10
Ni ≤ 1,00 ± 0,03
> 1,00 ≤ 5,0 ± 0,07
> 5,0 ≤ 10,0 ± 0,10
> 10,0 ≤ 20,0 ± 0,15
> 20,0 ≤ 27,0 ± 0,20
Cr+Mo+Ni ≤ 0,63 +0.05
Nb ≤ 1,25 ± 0,05
Nb+Ta ≥ 0,70 ≤ 1,20 ± 0,10
Ti ≤ 0,15 ± 0,01
> 0,15 ≤ 1,00 ± 0,05
> 1,00 ≤ 2,75 ± 0,10
V ≤ 0,05 ± 0,01
> 0,05 ≤ 0,80 ± 0,03
As ≤ 0,020 ± 0,003
Sn ≤ 0,020 ± 0,003
Feb ≤ 1,50 +0.05
> 1,50 ≤ 9,0 ± 0,10
  • a If several product analyses are carried out on one cast, and the contents of an individual element determined lie outside the permissible range of the chemical composition specified for the cast analysis, then it is only allowed to exceed the permissible maximum value or to fall short of the permissible minimum value, but not both for one cast.
  • b For nickel alloys.

EN 10269 X15CrMo5-1 Mechanical properties

Mechanical properties at Room Temperature

Mechanical properties at room temperature and at 20 °C of steels in delivery conditions which support the Essential Safety Requirements of Directive 97/23/EC b

Material designation Heat treatment condition
a		 Diameter c Proof strength Tensile strength Elongation after fracture Reduction in area Impact energy (ISO-V) at 20°C
Name Number
d
mm		 Rp0,2
MPa min.		 Rm
MPa		 A
%
min.		 Z
%
min.		 KV2
J
min.
X15CrMo5-1 1.739 +NT or +QT d< 160 420 640 to 780 14 45 40
  • a +AT = solution annealed; +C = cold work hardened; +N = normalized; +NT = normalized and tempered; +P = precipitation hardened;
  • +QT = quenched and tempered; +WW = warm worked (see Annex B).
  • b Products made of steel grades and these final heat treatment conditions support the Essential Safety Requirements of Directive 97/23/EC, see Annex 1, 7.5 of this directive.
  • c For rectangular cross-sections "d" will be replaced by "b" (see Figure 1).

EN 10269 Proof strength

Minimum 0,2 %-proof strength values at elevated temperature of steels in delivery conditions which support the Essential Safety Requirements of Directive 97/23/EC d

Material designation Heat treatment condition a Diameter e
d
mm		 Minimum 0,2 %-proof strength Rp0,2 in MPa at a temperature (in °C) of:
Name Number 50 100 150 200 250 300 350 400 450 500 550 600 650
X15CrMo5-1 1.7390 +NT or +QT d ≤ 160 392*) 345 335 327 323 322 316 306 285 256 - - -
  • a +AT = solution annealed; +C = cold work hardened; +N = normalized; +NT = normalized and tempered; +P = precipitation hardened; +QT = quenched and tempered; +WW = warm worked (see Annex B).
  • b This steel grade is generally not applied in the creep range.
  • c Values in brackets signify that the steel is not intended for use (and testing) at those temperatures.
  • d Products made to these steel grades and these final heat treatment conditions support the Essential Safety Requirements of Directive 97/23/EC; see Annex 1, 7.5 of this directive.
  • e For rectangular cross sections "d" will be replaced by "b" (see Figure 1).
  • *) Values calculated by linear interpolation.

Tests

Verification tests to be carried out and extent of testing

Test Test statusa Number of samples for batches of Number of test pieces per sample
≤ 10 t > 10 t to ≤ 15 t > 15 t
Chemical analysis cast m 1/cast (see 8.3.1 and 11.1)
product Ob (see 10.1.1)
Hardness test on homogeneity / shearing Oc (see 10.1.2 and 10.2.1.3)
Intergranular corrosion resistance Oc (see 11.6.5)
Tensile test at room temperature m 2 3 4 1
Tensile test at elevated temperature Od 1
Impact test at room temperature Me 3
Impact test at low temperature Of 3
Non-destructive testing Og not applicable
Verification of surface quality o
Other tests Mh
  • a Tests marked with a 'm' (mandatory) shall be carried out. In all cases, those marked with an 'o' (optional) shall be carried out as specific tests only if agreed at the time of enquiry and order.
  • b •• A product analysis (per cast) may be agreed at the time of enquiry and order; additionally a deviating extent of testing may be agreed.
  • c • The number of samples and test pieces per sample shall be agreed at time of enquiry and order.
  • d •• For verification of Rp0,2 and, in the case of austenitic steels and nickel alloys, of the tensile strength at elevated temperatures for products to be used at elevated temperatures.
  • e •• Optional for austenitic steels, except austenitic grades for cryogenic service (> 15 mm diameter or thickness).
  • f •• For materials for use at low temperatures.
  • g For verification of internal soundness.

EN 10269 X15CrMo5-1 Bolting Certifications

  • EN 10204 3.1
  • EN 10204 3.2
  • PED 2014/68/EC
  • MERKBLATT AD 2000 W2/W7/W10
  • API 20 E BSL 1/ BSL 2
  • NACE MR 0175
  • NACE MR 0103