Scope

EN 10269 Specification is a European Standard that specifies requirements for semi-finished products, bars and rods for fasteners with properties specified at elevated and/or low temperatures made of non-alloy and alloy (including stainless) steels and nickel alloys.
The requirements of this standard may be applied also to the finished fasteners.
The general technical delivery conditions in EN 10021 also apply to products supplied in accordance with this European Standard.
NOTE : Once this European Standard is published in the EU Official Journal (OJEU) under Directive 97/23/EC, presumption of conformity to the Essential Safety Requirements (ESRs) of Directive 97/23/EC is limited to technical data of materials in this European Standard and does not presume adequacy of the material to a specific item of equipment. Consequently, the assessment of the technical data stated in this material standard against the design requirements of this specific item of equipment to verify that the ESRs of Directive 97/23/EC are satisfied, needs to be done.

Related Specifications of EN 10269 Bolting

DIN 267 ISO 3506-5 BS EN 10088-3

EN 10269 Chemical composition

Cast Analysis A

Material designation Chemical composition, % by mass
Name Number C Si Mn P
max.		 S
max.		 Al tot B Cr Mo Ni V Others
Steels for quenching and tempering
20MnB4 1.5525 0,18 to 0,23 ≤ 0,30 0,90 to 1,20 0.025 0.025 ≥ 0,020 0,000 8 to 0,005 0 ≤ 0,30 - - - Cu ≤ 0,25
23MnB4 1.5535 0,20 to 0,25 ≤ 0,30 0,90 to 1,20 0.025 0.025 ≥ 0,020 0,000 8 to 0,005 0 ≤ 0,30 - - - Cu ≤ 0,25
23MnB3 1.5507 0,21 to 0,25 ≤ 0,15 0,80 to 1,00 0.015 0.015 0,02-
0,08		 0,000 8 to 0,005 0 0,25 to 0,35 - - - Cu ≤ 0,25
Ti ≤ 0,06
C35E 1.1181 0,32 to 0,39 ≤ 0,40 0,50 to 0,80 0.030 0,015 b - - ≤ 0,40 ≤ 0,10 ≤ 0,40 - Cr+Mo+Ni: ≤ 0,63
C45E 1.1191 0,42 to 0,50 ≤ 0,40 0,50 to 0,80 0.030 0,015 b - - ≤ 0,40 ≤ 0,10 ≤ 0,40 - Cr+Mo+Ni: ≤ 0,63
35B2 1.5511 0,32 to 0,39 ≤ 0,40 0,50 to 0,80 0.030 0,015 b ≥ 0,020 0,000 8 to 0,005 0 - - - - -
20Mn5 1.1133 0,17 to 0,23 ≤ 0,40 1,00 to 1,50 0.030 0.035 ≥ 0,020 - ≤ 0,40 ≤ 0,10 ≤ 0,40 - Cr+Mo+Ni: ≤ 0,63
25CrMo4 1.7218 0,22 to 0,29 ≤ 0,40 0,60 to 0,90 0.025 0.035 - - 0,90 to 1,20 0,15 to 0,30 - - -
42CrMo4 1.7225 0,38 to 0,45 ≤ 0,40 0,60 to 0,90 0.025 0.035 - - 0,90 to 1,20 0,15 to 0,30 - - -
42CrMo5-6 1.7233 0,39 to 0,45 ≤ 0,40 0,40 to 0,70 0.025 0.035 - - 1,20 to 1,50 0,50 to 0,70 - - -
40CrMoV4-6 1.7711 0,36 to 0,44 ≤ 0,40 0,45 to 0,85 0.025 0.030 ≤ 0,015 - 0,90 to 1,20 0,50 to 0,65 - 0,25 to 0,35 -
27NiCrMoV15-6 1.6957 0,22 to 0,32 c ≤ 0,15 0,15 to 0,40 0.010 0.007 - - 1,20 to 1,80 0,25 to 0,45 3,40 to 4,00 0,05 to 0,15 -
26 NiCrMo 14-6 1.6958 0,25 to 0,30 0,15 to
0,30		 0,20 to 0,50 0.020 0,015 b 0,005 to
0,050		 - 1,20 to 1,70 0,35 to 0,55 3,30 to 3,80 ≤ 0,12 -
21CrMoV5-7 1.7709 0,17 to 0,25 ≤ 0,40 0,40 to 0,80 0.025 0.030 ≤ 0,030 - 1,20 to 1,50 0,55 to 0,80 ≤ 0,60 0,20 to 0,35 -
20CrMoVTiB4-10 1.7729 0,17 to 0,23 ≤ 0,40 0,35 to 0,75 0.020 0,015 b 0,015 to
0,080		 0,001 to 0,010 0,90 to 1,20 0,90 to 1,10 ≤ 0,20 0,60 to 0,80 Ti: 0,07 to 0,15
As: ≤ 0,020
Sn: ≤ 0,020
Cu: ≤ 0,20
34CrNiMo6 1.6582 0,30 to 0,38 ≤ 0,40 0,50 to 0,80 0.025 0.035 - - 1,30 to 1,70 0,15 to 0,30 1,30 to 1,70 - -
30CrNiMo8 1.6580 0,26 to 0,34 ≤ 0,40 0,50 to 0,80 0.025 0.035 - - 1,80 to 2,20 0,30 to 0,50 1,80 to 2,20 - -
X12Ni5 1.5680 ≤ 0,15 ≤ 0,35 0,30 to 0,80 0.020 0.010 - - - - 4,75 to 5,25 ≤ 0,05 -
X8Ni9 1.5662 ≤ 0,10 ≤ 0,35 0,30 to 0,80 0.020 0.010 - - - ≤ 0,10 8,5 to 10,0 ≤ 0,05 -
X15CrMo5-1 1.7390 ≤ 0,18 ≤ 0,40 0,30 to 0,80 0.025 0.015 - - 4,0 to 6,0 0,45 to 0,65 - - -
X22CrMoV12-1 1.4923 0,18 to 0,24 ≤ 0,50 0,40 to 0,90 0.025 0,015 b - - 11,0 to 12,5 0,80 to 1,20 0,30 to 0,80 0,25 to 0,35 -
X12CrNiMoV12-3 1.4938 0,08 to 0,15 ≤ 0,50 0,40 to 0,90 0.025 0.015 11,0 to 12,5 1,50 to 2,00 2,00 to 3,00 0,25 to 0,40 N: 0,020 to 0,040
X19CrMoNbVN11-1 1.4913 0,17 to 0,23 ≤ 0,50 0,40 to 0,90 0.025 0.015 ≤ 0,020 ≤ 0,001 5 10,0 to 11,5 0,50 to 0,80 0,20 to 0,60 0,10 to 0,30 Nb: 0,25 to 0,55
N: 0,05 to 0,10
Austenitic steels
X2CrNi18-9 1.4307 ≤ 0,030 ≤ 1,00 ≤ 2,00 0.045 0,015 b - - 17,5 to 19,5 - 8,0 to 10,0 - N ≤ 0,10
X5CrNi18-10 1.4301 ≤ 0,07 ≤ 1,00 ≤ 2,00 0.045 0,015 b - - 17,0 to 19,5 - 8,0 to 10,5 - N ≤ 0,10
X4CrNi18-12 1.4303 ≤ 0,06 ≤ 1,00 ≤ 2,00 0.045 0,015 b - - 17,0 to 19,0 - 11,0 to 13,0 - N ≤ 0,10
X2CrNiN18-10 1.4311 ≤ 0,030 ≤ 1,00 ≤ 2,00 0.045 0,015 b - - 17,5 to 19,5 - 8,5 to 11,5 - N: 0,12 to 0,22
X6CrNi25-20 1.4951 0,04 to 0,08 ≤ 0,70 ≤ 2,00 0.035 0,015 b - - 24,0 to 26,0 - 19,0 to 22,0 - N ≤ 0,10
X2CrNiMo17-12-2 1.4404 ≤ 0,030 ≤ 1,00 ≤ 2,00 0.045 0,015 b - - 16,5 to 18,5 2,00 to 2,50 10,0 to 13,0 - N ≤ 0,10
X5CrNiMo17-12-2 1.4401 ≤ 0,07 ≤ 1,00 ≤ 2,00 0.045 0,015 b - - 16,5 to 18,5 2,00 to 2,50 10,0 to 13,0 - N ≤ 0,10
X2CrNiMoN17-13-3 1.4429 ≤ 0,030 ≤ 1,00 ≤ 2,00 0.045 0.015 - - 16,5 to 18,5 2,50 to 3,00 11,0 to 14,0 - N: 0,12 to 0,22
X3CrNiCu18-9-4 1.4567 ≤ 0,04 ≤ 1,00 ≤ 2,00 0.045 0,015 b - - 17,0 to 19,0 - 8,5 to 10,5 - N ≤ 0,10
Cu: 3,0 to 4,0
X6CrNi18-10 1.4948 0,04 to 0,08 ≤ 1,00 ≤ 2,00 0.035 0.015 - - 17,0 to 19,0 - 8,0 to 11,0 - N ≤ 0,10
X10CrNiMoMnNbVB15-10-1 1.4982 0,07 to 0,13 ≤ 1,00 5,50 to 7,00 0.040 0,015 b - 0,003 to 0,009 14,0 to 16,0 0,80 to 1,20 9,0 to 11,0 0,15 to 0,40 Nb: 0,75 to 1,25
N ≤ 0,10
X3CrNiMoBN17-13-3 1.4910 ≤ 0,04 ≤ 0,75 ≤ 2,00 0.035 0.015 - 0,001 5 to
0,005 0		 16,0 to 18,0 2,00 to 3,00 12,0 to 14,0 - N: 0,10 to 0,18
X6CrNiMoB17-12-2 1.4919 0,04 to 0,08 ≤ 1,00 ≤ 2,00 0.035 0.015 - 0,001 5 to
0,005 0		 16,5 to 18,5 2,00 to 2,50 10,0 to 13,0 - N ≤ 0,10
X6CrNiTiB18-10 1.4941 0,04 to 0,08 ≤ 1,00 ≤ 2,00 0.035 0.015 - 0,001 5 to
0,005 0		 17,0 to 19,0 - 9,0 to 12,0 - Ti: 5 x C to 0,80
X6NiCrTiMoVB25-15- 2 1.4980 0,03 to 0,08 ≤ 1,00 1,00 to 2,00 0.025 0.015 ≤ 0,35 0,003 0 to 0,010 13,5 to 16,0 1,00 to 1,50 24,0 to 27,0 0,10 to 0,50 Ti: 1,90 to 2,30
X7CrNiMoBNb16-16 1.4986 0,04 to 0,10 0,30 to 0,60 ≤ 1,50 0.045 0,015 b - 0,05 to 0,10 15,5 to 17,5 1,60 to 2,00 15,5 to 17,5 - Nb+Ta: 10 x C to 1,20
Nickel alloys
NiCr20TiAl 2.4952 0,04 to 0,10 ≤ 1,00 ≤ 1,00 0.020 0.015 1,00 to 1,80 ≤ 0,008 18,0 to 21,0 - ≥ 65 - Co ≤ 1,00, Cu ≤ 0,20
Ti: 1,80 to 2,70
Fe ≤ 1,50
NiCr19Fe19Nb5Mo3 2.4668 0,02 to 0,08 ≤ 0,035 ≤ 0,035 0.015 0.015 0,30 to 0,70 0,002 to 0,006 17,0 to 21,0 2,80 to 3,30 50,00 to 55,00 - Cu ≤ 0,30 ; Co ≤ 1,00 Nb: 4,70 to 5,50
Ti: 0,60 to 1,20
Fe: Remaining
NiCr15Fe7TiAl 2.4669 ≤ 0,08 ≤ 0,50 ≤ 1,00 0.020 0.015 0,40 to 1,00 - 14,0 to 17,0 - ≥ 70 - Co ≤ 1,00, Cu ≤ 0,50
Ti: 2,25 to 2,75
Nb+Ta: 0,70 to 1,20
Fe: 5,0 to 9,0
  • a Elements not listed in this table may not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. All appropriate precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production which would impair mechanical properties and the usefulness of the steel.
  • b A controlled sulphur content of 0,015 % to 0,030 % improves the machinability and is therefore recommended and may be agreed at time of enquiry and order. For weldability, a controlled sulphur content of 0,008 % to 0,030 % is recommended and may be agreed at time of enquiry and order.
  • c For requirements regarding magnetic properties up to a maximum of 0,28 % C.

Permissible product analysis tolerances on the limiting values given in for the cast analysis

Element(s) Specified limits, cast analysis
% by mass		 Permissible tolerance a
% by mass
C < 0,03 ± 0,005
≥ 0,03 ≤ 0,20 ± 0,01
> 0,20 ≤ 0,50 ± 0,02
Si ≤ 0,40 ± 0,03
> 0,40 ≤ 1,00 ± 0,05
Mn ≤ 2,00 ± 0,04
> 2,00 ≤ 7,0 ± 0,10
P ≤ 0,045 +0.005
S ≤ 0,015 +0.003
> 0,015 ≤ 0,035 +0.005
N ≤ 0,040 ± 0,005
> 0,040 ≤ 0,18 ± 0,01
Al ≥ 0,015 ≤ 0,08 +0,01
-0,005
> 0,08 ≤ 0,35 ± 0,05
> 0,35 ≤ 1,80 ± 0,10
B ≤ 0,010 ± 0,000 5
> 0,010 ≤ 0,10 ± 0,005
Cr ≤ 2,00 ± 0,05
> 2,00 < 10,0 ± 0,10
≥ 10,0 < 15,0 ± 0,15
≥ 15,0 ≤ 21,0 ± 0,20
Cu ≤ 0,50 +0.05
> 0,50 ≤ 4,0 ± 0,10
Mo ≤ 0,60 ± 0,03
> 0,60 < 1,75 ± 0,05
≥ 1,75 ≤ 3,00 ± 0,10
Ni ≤ 1,00 ± 0,03
> 1,00 ≤ 5,0 ± 0,07
> 5,0 ≤ 10,0 ± 0,10
> 10,0 ≤ 20,0 ± 0,15
> 20,0 ≤ 27,0 ± 0,20
Cr+Mo+Ni ≤ 0,63 +0.05
Nb ≤ 1,25 ± 0,05
Nb+Ta ≥ 0,70 ≤ 1,20 ± 0,10
Ti ≤ 0,15 ± 0,01
> 0,15 ≤ 1,00 ± 0,05
> 1,00 ≤ 2,75 ± 0,10
V ≤ 0,05 ± 0,01
> 0,05 ≤ 0,80 ± 0,03
As ≤ 0,020 ± 0,003
Sn ≤ 0,020 ± 0,003
Feb ≤ 1,50 +0.05
> 1,50 ≤ 9,0 ± 0,10
  • a If several product analyses are carried out on one cast, and the contents of an individual element determined lie outside the permissible range of the chemical composition specified for the cast analysis, then it is only allowed to exceed the permissible maximum value or to fall short of the permissible minimum value, but not both for one cast.
  • b For nickel alloys.

EN 10269 Mechanical properties

Mechanical properties at Room Temperature

Mechanical properties at room temperature for delivery conditions normally applied for further processing

Material designation Heat treatment condition a,b Hardness
HBW
max.		 Tensile strength
Rm
MPa
max.		 Reduction in area
Z
%
min.
Name Number
20MnB4 1.5525 +AC - 520 64
23MnB4 1.5535 +AC - 520 64
23MnB3 1.5507 +AC - 520 64
35B2 1.5511 +AC - 570 62
25CrMo4 1.7218 +S 255 - -
+A 212 - -
+AC - 580 59
42CrMo4 1.7225 +S 255 - -
+A 241 - -
+AC - 630 57
42CrMo5-6 1.7233 +S 255 - -
+A 241 - -
40CrMoV4-6 1.7711 +A 241 - -
21CrMoV5-7 1.7709 +S 255 - -
+AC 229 - -
34CrNiMo6 1.6582 +A 255 - -
30CrNiMo8 1.6580 +A 255 - -
X22CrMoV12-1 1.4923 +A 302 - -
X12CrNiMoV12-3 1.4938 +A 311 - -
X19CrMoNbVN11-1 1.4913 +A 302 - -
  • a + AC = annealed to achieve spheroidized carbides; + S = treated for cold shearing; + A = soft annealed.
  • b Products made to these heat treatment conditions do not support the Essential Safety Requirements of Directive 97/23/EC, unless other criteria are taken into account, see Annex 1, 7.5 of this directive.

Mechanical properties at room temperature and at 20 °C of steels in delivery conditions which support the Essential Safety Requirements of Directive 97/23/EC b

Material designation Heat treatment condition
a		 Diameter c Proof strength Tensile strength Elongation after fracture Reduction in area Impact energy (ISO-V) at 20°C
Name Number
d
mm		 Rp0,2
MPa min.		 Rm
MPa		 A
%
min.		 Z
%
min.		 KV2
J
min.
20MnB4 1.5525 +QT d ≤ 16 640 800 to 950 14 52 40
23MnB4 1.5535 +QT d ≤ 24 640 800 to 950 14 52 40
23MnB3 1.5507 +QT d ≤ 16 640 800 to 950 14 52 40
C35E 1.1181 +N d ≤ 60 300 500 to 650 20 - 27
+QT d ≤ 60 300 500 to 650 22 45 55
60 < d ≤ 150 300 500 to 650 22 45 39
C45E 1.1191 +N d ≤ 60 340 560 to 710 17 - 27
+QT d ≤ 60 340 560 to 710 19 40 50
60 <di 150 340 560 to 710 19 40 35
35B2 1.5511 +QT d ≤ 60 300 500 to 650 22 45 55
60 <di 150 300 500 to 650 22 45 39
20Mn5 1.1133 +N d ≤ 60 320 500 to 650 22 55 55
60 <di 150 300 500 to 650 20 55 55
25CrMo4 1.7218 +QT d ≤ 100 440 600 to 750 18 60 60
100< di 150 420 600 to 750 18 60 45
42CrMo4 1.7225 +QT d ≤ 65 730 860 to 1 060 14 50 50
42CrMo5-6 1.7233 +QT d ≤ 100 700 860 to 1 060 16 50 50
100 < d ≤ 150 640 850 to 1 000 16 50 40
40CrMoV4-6 1.7711 +QT d ≤ 100 700 850 to 1 000 14 45 40
100 < d ≤ 150 640 850 to 1 000 14 45 40
27NiCrMoV15-6 1.6957 +QT d ≤ 160 700 850 to 1 000 16 40 63
26 NiCrMo-14-6 1.6958 +QT d ≤ 70 940 1 040 to 1 240 14 50 55
70<d ≤ 160 36
21CrMoV5-7 1.7709 +QT d ≤ 160 550 700 to 850 16 60 63
20CrMoVTiB4-10 1.7729 +QT d ≤ 100 660 820 to 1 000 15 50 40
100 < d ≤ 160 660 820 to 1 000 15 50 27
34CrNiMo6 1.6582 +QT d ≤ 40 940 1 040 to 1 200 14 40 45
40 < d ≤ 120 640 min. 800 14 52 45
30CrNiMo8 1.658 +QT d ≤ 40 940 1040 to 1 200 14 40 45
40 < d ≤ 120 640 min. 800 14 52 45
X12Ni5 1.568 (+N), +NT or +QT d ≤ 40 390 530 to 710 19 50 70
40 < d ≤ 75 380 530 to 710 19 50 70
X8Ni9 1.5662 +N+NT (or +QT) d ≤ 40 490 640 to 840 18 50 70
40 < d ≤ 75 480 640 to 840 18 50 70
+QT d ≤ 40 585 680 to 820 18 50 120
40 < d ≤ 75 575 680 to 820 18 50 120
X15CrMo5-1 1.739 +NT or +QT d< 160 420 640 to 780 14 45 40
X22CrMoV12-1 1.4923 +QT1 d< 160 600 800 to 950 14 40 27
X12CrNiMoV12-3 1.4938 +QT d< 160 760 930 to 1 130 14 40 40
Austenitic stees
X2CrNi18-9 1.4307 +AT d< 160 175 450 to 680 45 - 100
+C700 d ≤ 35 350 700 to 850 20 - 80
X5CrNi18-10 1.4301 +AT d< 160 190 500 to 700 45 - 100
+C700 d ≤ 35 350 700 to 850 20 - 80
X4CrNi18-12 1.4303 +AT d< 160 190 500 to 700 45 - 100
+C700 d ≤ 35 350 700 to 850 20 - 80
X2CrNiN18-10 1.4311 +AT d< 160 270 550 to 760 40 - 100
X6CrNi25-20 1.4951 +AT d< 160 200 510 to 750 35 - 100
X2CrNiMo17-12-2 1.4404 +AT d< 160 200 500 to 700 40 - 100
+C700 d ≤ 35 350 700 to 850 20 - 80
X5CrNiMo17-12-2 1.4401 +AT d< 160 200 500 to 700 40 - 100
+C700 d ≤ 35 350 700 to 850 20 - 80
X2CrNiMoN17-13-3 1.4429 +AT d< 160 280 580 to 800 40 - 100
X3CrNiCu18-9-4 1.4567 +AT d< 160 175 450 to 650 45 - 100
+C700 d ≤ 35 350 700 to 850 20 - 80
X6CrNi18-10 1.4948 +AT d< 160 185 500 to 700 40 - 90
X10CrNiMoMnNbVB15-10-1 1.4982 +AT+WW d ≤ 100 510 650 to 850 25 - 50
X3CrNiMoBN17-13-3 1.491 +AT d< 160 260 550 to 750 35 - 100
X6CrNiMoB17-12-2 1.4919 +AT d< 160 205 490 to 690 35 - 100
X6CrNiTiB 18-10 1.4941 +AT d< 160 195 490 to 680 35 - 100
X6NiCrTiMoVB25-15-2 1.498 +AT+P d< 160 600 900 to 1 150 15 - 50
X7CrNiMoBNb16-16 1.4986 +WW+P d ≤ 100 500 650 to 850 16 - 50
  • a +AT = solution annealed; +C = cold work hardened; +N = normalized; +NT = normalized and tempered; +P = precipitation hardened;
  • +QT = quenched and tempered; +WW = warm worked (see Annex B).
  • b Products made of steel grades and these final heat treatment conditions support the Essential Safety Requirements of Directive 97/23/EC, see Annex 1, 7.5 of this directive.
  • c For rectangular cross-sections "d" will be replaced by "b" (see Figure 1).

Mechanical properties at room temperature and at 20°C of steels and nickel alloys in delivery conditions which do not support the Essential Safety Requirements of Directive 97/23/EC b

Material designation Heat treatment condition
a		 Diameter c Proof strength Tensile strength Elongation after fracture Reduction in area Impact energy (ISO-V) at 20°C
Name Number
d
mm		 Rp0,2
MPa min.		 Rm
MPa		 A
%
min.		 Z
%
min.		 KV2
J
min.
Steels for quenching and tempering
X22CrMoV12-1 1.4923 +QT2 d ≤ 160 700 900 to 1 050 11 35 20
X19CrMoNbVN11-1 1.4913 +QT d ≤ 160 750 900 to 1 050 12 40 20
Austenitic steels
X2CrNi18-9 1.4307 +C800 d ≤ 25 500 800 to 1 000 12 - 80
X4CrNi18-12 1.4303 +C800 d ≤ 25 500 800 to 1 000 12 - 80
X2CrNiMo17-12-2 1.4404 +C800 d ≤ 25 500 800 to 1 000 12 - 80
X5CrNiMo17-12-2 1.4401 +C800 d ≤ 25 500 800 to 1 000 12 - 80
Nickel alloys
NiCr19Fe19Nb5Mo3 2.4668 +P d ≤ 160 1030 min. 1 230 12 - 12
NiCr20TiAl 2.4952 +AT+P d ≤ 160 600 1 000 to 1 300 12 12 20
NiCr15Fe7TiAl 2.4669 +AT+P d ≤ 25 650 1 000 to 1 200 20 28 22
  • a +AT = solution annealed; +C = cold work hardened; +N = normalized; +NT = normalized and tempered; +P = precipitation hardened;
  • +QT = quenched and tempered; +WW = warm worked (see Annex B).
  • b Products made to these steel grades and these final heat treatment conditions do not support the Essential Safety Requirements of Directive 97/23/EC, unless other criteria are taken into account; see Annex 1, 7.5 of this directive.
  • c For rectangular cross-sections "d" will be replaced by "b"

EN 10269 Proof strength

Minimum 0,2 %-proof strength values at elevated temperature of steels in delivery conditions which support the Essential Safety Requirements of Directive 97/23/EC d

Material designation Heat treatment condition a Diameter e
d
mm		 Minimum 0,2 %-proof strength Rp0,2 in MPa at a temperature (in °C) of:
Name Number 50 100 150 200 250 300 350 400 450 500 550 600 650
Steels for quenching and tempering
C35E 1.1181 +N d ≤ 60 289*) 270*) 251 229 213 192 182 173 - - - - -
+QT d ≤ 60 289*) 270*) 251 229 213 192 182 173 - - - - -
60 < d ≤ 150 287*) 264*) 242*) 220 203 186 167 147 - - - - -
C45E 1.1191 +QT d ≤ 150 330*) 314 299*) 284 255 235 206 - - - - - -
35B2 1.5511 +QT d ≤ 60 289*) 270*) 251 229 213 192 182 173 - - - - -
60 < d ≤ 150 287*) 264*) 242*) 220 203 186 167 147 - - - - -
20Mn5 1.1133 +N d ≤ 60 306*) 283*) 260 237 213 192 182 173 - - - - -
60 < d ≤ 150 304*) 278*) 251 229 213 192 182 173 - - - - -
25CrMo4 1.7218 +QT d ≤ 100 435*) 428*) 420*) 412 392 363 333 304 275 235 - - -
100 < d ≤ 150 414*) 403*) 393*) 382 372 344 324 294 265 226 - - -
42CrMo4 1.7225 +QT d ≤ 60 720*) 702 677 640 602 562 518 475 420 375 - - -
42CrMo5-6 1.7233 + QT d ≤ 100 681*) 662 639 616 601 585 570 547 516 462 362 223 -
100 < d ≤ 150 625*) 605 584 563 549 535 521 500 472 422 331 204 -
40CrMoV4-6 1.7711 +QT d ≤ 100 687*) 670 647 631 608 593 577 554 523 470 400 293 -
100 < d ≤ 160 631*) 612 591 577 556 542 528 507 479 429 366 268 -
27NiCrMoV15-6 1.6957 +QT d ≤ 160 - 660 - 625 600 580 550 (510) c (460) c (400) c - - -
26 NiCrMo14-6 1.6958 +QT 70 < d ≤ 160 - 853 843 834 804 785 765 - - - - - -
21CrMoV5-7 1.7709 +QT d ≤ 160 542*) 530 515*) 500 480*) 460 435*) 410 380 350 - - -
20CrMoVTiB4-10 1.7729 +QT d ≤ 160 642*) 624 603 595 581 573 559 537 508 464 406 334 -
X15CrMo5-1 1.7390 +NT or +QT d ≤ 160 392*) 345 335 327 323 322 316 306 285 256 - - -
X22CrMoV12-1 1.4923 +QT1 d ≤ 160 585*) 560 545*) 530 505*) 480 450*) 420 380 335 - - -
X12CrNiMoV12-3 b 1.4938 +QT1 d ≤ 160 730*) 680 668*) 655 653*) 650 630*) 610 560 505 400 - -
Austenitic steels
X2CrNi18-9 1.4307 +AT d ≤ 160 164*) 145 130 118 108 100 94 89 85 81 80 - -
X5CrNi18-10 1.4301 +AT d ≤ 160 177*) 155 140 127 118 110 104 98 95 92 90 - -
X4CrNi18-12 1.4303 +AT d ≤ 160 177*) 155 140 127 118 110 104 98 95 92 90 - -
X2CrNiN18-10 1.4311 +AT d ≤ 160 246 205 175 157 145 136 130 125 121 119 118 - -
X6CrNi25-20 1.4951 +AT d ≤ 160 177 140 128 116 108 100 94 91 86 85 84 - -
X2CrNiMo17-12-2 1.4404 +AT d ≤ 160 187*) 165 150 137 127 119 113 108 103 100 98 - -
X5CrNiMo17-12-2 1.4401 +AT d ≤ 160 191*) 175 158 145 135 127 120 115 112 110 108 - -
X2CrNiMoN17-13-3 1.4429 +AT d ≤ 160 256*) 215 195 175 165 155 150 145 140 138 136 - -
X6CrNi18-10 1.4948 +AT d ≤ 160 174*) 157 142 127 117 108 103 98 93 88 83 78 -
X10CrNiMoMnNbVB15-10-1 1.4982 +AT+WW d ≤ 100 490 463 446 434 423 413 405 396 391 386 378 365 346
X3CrNiMoBN17-13-3 1.4910 +AT d ≤ 160 239*) 205 187 170 159 148 141 134 130 127 124 121 -
X6CrNiMoB17-12-2 1.4919 +AT d ≤ 160 194*) 177 162 147 137 127 122 118 113 108 103 98 -
X6CrNiTiB18-10 1.4941 +AT d ≤ 160 183*) 162 152 142 137 132 127 123 118 113 108 103 -
X6NiCrTiMoVB25-15-2 1.4980 +AT+P d ≤ 160 592*) 580 570 560 550 540 530 520 510 490 460 430 380
X7CrNiMoBNb16-16 1.4986 +WW+P d ≤ 100 489*) 470*) 451*) 432 412 393 372 353 334 314 284 255 206
  • a +AT = solution annealed; +C = cold work hardened; +N = normalized; +NT = normalized and tempered; +P = precipitation hardened; +QT = quenched and tempered; +WW = warm worked (see Annex B).
  • b This steel grade is generally not applied in the creep range.
  • c Values in brackets signify that the steel is not intended for use (and testing) at those temperatures.
  • d Products made to these steel grades and these final heat treatment conditions support the Essential Safety Requirements of Directive 97/23/EC; see Annex 1, 7.5 of this directive.
  • e For rectangular cross sections "d" will be replaced by "b" (see Figure 1).
  • *) Values calculated by linear interpolation.

Minimum 0,2 %-proof strength values at elevated temperature of steels and nickel alloys in delivery conditions which do not support the Essential Safety Requirements of Directive 97/23/EC b

Material designation Heat treatment condition a Diameter c
d
mm		 Minimum 0,2 %-proof strength Rp0,2 in MPa at a temperature (in °C) of:
Name Number 50 100 150 200 250 300 350 400 450 500 550 600 650
Steels for quenching and tempering
X22CrMoV12-1 1.4923 +QT2 d ≤160 681*) 650 625*) 600 575*) 550 518*) 485 440 390 - - -
X19CrMoNbVN11-1 1.4913 +QT d ≤ 160 726*) 701 676 651 643 627 610 577 544 495 412 305 -
Nickel alloys
NiCr20TiAl 2.4952 +AT+P d ≤ 160 595*) 586*) 577*) 568 564 560 550 540 530 520 510 500 480
NiCr19Fe19Nb5Mo3 2.4668 +P d ≤ 160 - - - - - 880 - 865 - 860 - 860 -
NiCr15Fe7TiAl 2.4669 +AT+P d ≤ 25 625*) 620 615 610 606 601 596 592 587 582 578 573 565
  • a +AT = solution annealed; +C = cold work hardened; +N = normalized; +NT = normalized and tempered; +P = precipitation hardened; +QT = quenched and tempered; +WW = warm worked (see Annex B).
  • b Products made to these steel grades and these final heat treatment conditions do not support the Essential Safety Requirements of Directive 97/23/EC, unless other criteria are taken into account; see Annex 1, 7.5 of this directive.
  • c For rectangular cross sections "d" will be replaced by "b".
  • *) Values calculated by linear interpolation.

EN 10269 Tensile Strength

Minimum tensile strength values at elevated temperatures of steels in delivery conditions which support the Essential Safety Requirements of Directive 97/23/EC b

Material designation Heat treatment condition a Diameter c
d
mm		 Minimum tensile strength Rm in MPa at a temperature (in °C) of:
Name Number 50 100 150 200 250 300 350 400 450 500 550 600 650
Austenitic steels
X2CrNi18-9 1.4307 +AT d ≤ 160 440 410 380 360 350 340 340 330 - - - - -
X5CrNi18-10 1.4301 +AT d ≤ 160 480 450 420 400 390 380 380 380 375 360 335 300 -
X4CrNi18-12 1.4303 +AT d  160 480 450 420 400 390 380 380 380 375 360 335 300 -
X2CrNiN18-10 1.4311 +AT d ≤ 160 527 490 460 430 420 410 410 - - - - - -
X6CrNi25-20 1.4951 +AT d ≤ 160 495 470 450 430 420 410 405 400 385 370 350 320 -
X2CrNiMo17-12-2 1.4404 +AT d ≤ 160 460 430 410 390 385 380 380 380 375 360 335 - -
X5CrNiMo17-12-2 1.4401 +AT d ≤ 160 480 460 440 420 415 410 410 410 405 390 375 350 -
X2CrNiMoN17-13-3 1.4429 +AT d ≤ 160 550 520 490 460 450 440 435 435 435 430 410 380 -
X6CrNi18-10 1.4948 +AT d ≤ 160 480 450 420 400 390 380 380 380 375 360 335 300 -
X10CrNiMoMnNbVB15-10-1 1.4982 +AT+WW d ≤ 100 610 565 530 505 490 475 465 460 450 440 430 410 390
X3CrNiMoBN17-13-3 1.4910 +AT d ≤ 160 550 520 490 460 450 440 435 435 435 430 410 380 -
X6CrNiMoB17-12-2 1.4919 +AT d ≤ 160 490 460 440 420 415 410 410 410 405 390 375 350 -
X7CrNiTiB18-10 1.4941 +AT d ≤ 160 490 460 440 420 415 410 410 410 405 390 375 350 -
X6NiCrTiMoVB25-15-2 1.4980 +AT+P d ≤ 160 - - - - - - - 720 710 700 690 670 -
X7CrNiMoBNb16-16 1.4986 +WW+P d ≤ 100 635 615 590 570 550 530 505 485 460 440 420 395 375
  • a +AT = solution annealed; +C = cold work hardened; +N = normalized; +NT = normalized and tempered; +P = precipitation hardened; +QT = quenched and tempered; +WW = warm worked (see Annex B).
  • b Products made to these steel grades and these final heat treatment conditions support the Essential Safety Requirements of Directive 97/23/EC; see Annex 1, 7.5 of this directive.
  • c For rectangular cross-sections "d" will be replaced by "b"

Minimum tensile strength values at elevated temperatures of nickel alloys in delivery conditions which do not support the Essential Safety Requirements of Directive 97/23/EC b

Material designation Heat treatment condition a Diameter c
d
mm		 Minimum tensile strength Rm in MPa at a temperature (in °C) of:
Name Number 50 100 150 200 250 300 350 400 450 500 550 600 650
Nickel alloys
NiCr19Fe19Nb5Mo3 2.4668 +P d ≤ 160 - - - - - - - - - - - - -
NiCr20TiAl 2.4952 +AT+P d ≤ 160 1000 975 950 900 900 900 900 900 900 890 880 850 -
NiCr15Fe7TiAl 2.4669 +AT+P d ≤ 25 1000 975 950 900 900 900 900 900 900 890 880 850 -
  • a +AT = solution annealed; +C = cold work hardened; +N = normalized; +NT = normalized and tempered; +P = precipitation hardened; +QT = quenched and tempered; +WW = warm worked (see Annex B).
  • b Products made to these steel grades and these final heat treatment conditions do not support the Essential Safety Requirements of Directive 97/23/EC, unless other criteria are taken into account; see Annex 1, 7.5 of this directive.
  • c For rectangular cross-sections "d" will be replaced by "b"

EN 10269 Impact Energy

Minimum impact energy (longitudinal direction) at low temperature of steels in delivery conditions which support the Essential Safety Requirements of Directive 97/23/EC b

Material designation Heat treatment condition a Diameter e
d
mm		 Minimum impact energy KV2 in J c
(ISO-V test piece) at a test temperature in °C of:
Name Number -270 -196 -160 -140 -120 -110 -100 -90 -80 -70 -60 -50 -40 -20 0 +20
Steels for quenching and tempering
20MnB4 1.5525 +QT d ≤ 16 - - - - - - - - - - 27 - - 40 40 40
23MnB4 1.5535 +QT d ≤ 24 - - - - - - - - - - 27 - - 40 40 40
23MnB3 1.5507 +QT d ≤ 16 - - - - - - - - - - 27 - - 40 40 40
20Mn5 1.1133 +N d ≤ 60 - - - - - - - - - - - 27 31 47 55 55
60 < d ≤ 150 - - - - - - - - - - - - - 40 55 55
25CrMo4 1.7218 +QT d ≤ 60 - - - - - - - - - - 40 40 45 50 - 60
60 < d ≤ 100 - - - - - - - - - - 40 40 50 - 60
42CrMo4 1.7225 +QT d ≤ 60 - - - - - - 27 - - - - - 40 - - 50
34CrNiMo6 1.6582 +QT d ≤ 100 - - - - - - - - - - - - 40 - - 45
30CrNiMo8 1.6580 +QT d ≤ 100 - - - - - - - - - - - - 40 - - 45
X12Ni5 1.5680 (+N), +NT d ≤ 40 - - - - 40 45 50 55 60 60 65 65 65 70 70 70
40 < d  75 - - - - - - - 50 55 60 60 65 65 65 70
X8Ni9 1.5662 +N +NT (or
+QT)		 d  75 - 40 45 50 50 - 60 - 70 70 70 70 70 70 70 70
+QT d  75 - 70 - - 100 - 110 - 120 120 120 120 120 120 120 120
Austenitic steels
X2CrNi18-9 1.4307 +C700 d ≤ 35 - 50 - - - - - - - - - - - - - 80
X5CrNi18-10 1.4301 +AT d ≤ 160 - 60 - - - - - - - - - - - - - 100
+C700 d ≤ 35 - 50 - - - - - - - - - - - - - 80
X4CrNi18-12 1.4303 +AT d ≤ 160 - 60 - - - - - - - - - - - - - 100
+C700 d ≤ 35 - 50 - - - - - - - - - - - - - 80
X2CrNiN18-10 1.4311 +AT d ≤ 160 - 60 - - - - - - - - - - - - - 100
X6CrNi25-20 1.4951 +AT d ≤ 160 - - - - - - - - - - - - - - - 100
X2CrNiMo17-12-2 1.4404 +C700 d  35 - 50 - - - - - - - - - - - - - 80
X5CrNiMo17-12-2 1.4401 +C700 d  35 - 50 - - - - - - - - - - - - - 80
X2CrNiMoN17-13-3 1.4429 +AT d ≤ 160 50 60 - - - - - - - - - - - - - 100
X6CrNi18-10 1.4948 +AT d ≤ 160 - 60 - - - - - - - - - - - - - 100
X3CrNiMoBN17-13-3 1.4910 +AT d ≤ 160 50 60 - - - - - - - - - - - - - 100
X6CrNiMoB17-12-2 1.4919 + AT d ≤ 160 - 60 - - - - - - - - - - - - - 100
X6CrNiTiB18-10 1.4941 + AT d ≤ 160 - 60 - - - - - - - - - - - - - 100
X6NiCrTiMoVB25-15-2 1.4980 d +AT+P d ≤ 160 - 40 - - - - - - - - - - - - - 50
  • a +AT = solution annealed; +C = cold work hardened; +N = normalized; +NT = normalized and tempered; +P = precipitation hardened; +QT = quenched and tempered; +WW = warm worked (see Annex B).
  • b Products made to these steel grades and these final heat treatment conditions support the Essential Safety Requirements of Directive 97/23/EC; see Annex 1, 7.5 of this directive.
  • c Average of 3 test results.
  • d Steel grade 1.4980 may be ordered for cryogenic purposes with impact values of 50 J at -270 °C, 60 J at -196 °C and 70 J at 20 °C.
  • e For rectangular cross sections "d" will be replaced by "b"

Minimum impact energy (longitudinal direction) at low temperature of nickel alloys in delivery conditions which do not support the Essential Safety Requirements of Directive 97/23/EC b

Material designation Heat treatment condition a Diameter d
d
mm		 Minimum impact energy KV2 in J c
(ISO-V test piece) at a test temperature in °C of:
Name Number -270 -196 -160 -140 -120 -110 -100 -90 -80 -70 -60 -50 -40 -20 0 +20
Nickel alloys
NiCr19Fe19Nb5Mo3 2.4668 +P d ≤160 - - - - - - - - - - - - - - - 12
NiCr20TiAl 2.4952 +AT+P d ≤160 - 20 - - - - - - - - - - - - - 20
NiCr15Fe7TiAl 2.4669 +AT+P d ≤ 25 - 20 - - - - - - - - - - - - - 22
  • a +AT = solution annealed; +C = cold work hardened; +N = normalized; +NT = normalized and tempered; +P = precipitation hardened; +QT = quenched and tempered; +WW = warm worked (see Annex B).
  • b Products made to these steel grades and these final heat treatment conditions do not support the Essential Safety Requirements of Directive 97/23/EC; see Annex 1, 7.5 of this directive.
  • c Average of 3 test results.
  • d For rectangular cross sections "d" will be replaced by "b"

Tests

Verification tests to be carried out and extent of testing

Test Test statusa Number of samples for batches of Number of test pieces per sample
≤ 10 t > 10 t to ≤ 15 t > 15 t
Chemical analysis cast m 1/cast (see 8.3.1 and 11.1)
product Ob (see 10.1.1)
Hardness test on homogeneity / shearing Oc (see 10.1.2 and 10.2.1.3)
Intergranular corrosion resistance Oc (see 11.6.5)
Tensile test at room temperature m 2 3 4 1
Tensile test at elevated temperature Od 1
Impact test at room temperature Me 3
Impact test at low temperature Of 3
Non-destructive testing Og not applicable
Verification of surface quality o
Other tests Mh
  • a Tests marked with a 'm' (mandatory) shall be carried out. In all cases, those marked with an 'o' (optional) shall be carried out as specific tests only if agreed at the time of enquiry and order.
  • b •• A product analysis (per cast) may be agreed at the time of enquiry and order; additionally a deviating extent of testing may be agreed.
  • c • The number of samples and test pieces per sample shall be agreed at time of enquiry and order.
  • d •• For verification of Rp0,2 and, in the case of austenitic steels and nickel alloys, of the tensile strength at elevated temperatures for products to be used at elevated temperatures.
  • e •• Optional for austenitic steels, except austenitic grades for cryogenic service (> 15 mm diameter or thickness).
  • f •• For materials for use at low temperatures.
  • g For verification of internal soundness.

EN 10269 Bolting Certifications

  • EN 10204 3.1
  • EN 10204 3.2
  • PED 2014/68/EC
  • MERKBLATT AD 2000 W2/W7/W10
  • API 20 E BSL 1/ BSL 2
  • NACE MR 0175
  • NACE MR 0103